In this work, methylcellulose (MC) was produced from bacterial cellulose (BC), using dimethyl sulfate in a 3 h (MC3h) or 5 h (MC5h) reaction under heterogeneous conditions, with reagent substitution at each hour. MC3h showed a degree of substitution (DS) of 2.26 ± 0.13 and MC5h showed a DS of 2.33 ± 0.05. The two samples were characterized by Fourier transform infrared spectroscopy (FTIR), X-ray powder diffraction (XRD), differential thermal analysis (DTA), thermal gravimetric analysis (TGA), 13C nuclear magnetic ressonance (NMR) and 1H NMR techniques. The FTIR spectra of the BC and MC samples present significant differences in the regions from 3750 to 2750 cm−1 and from 1500 to 750 cm−1, which evidence the methylation of the samples. Solid state NMR spectroscopy of the MC samples was used to identify the 13C NMR signals of substitution at sites C-2, C-3 or C-6 in the glucopyranose units. The modification of bacterial cellulose produced a material with a high DS, determined by three different techniques (chemically and using the liquid 1H and solid 13C NMR spectra). These samples also demonstrate high crystallinity and thermal stability. With the MC samples synthesized in this work, transparent and resistant films were prepared and also a highly porous sponge like material.

Membranas de poliamidas alifáticas são muito utilizadas como barreiras seletivas em processos de microfiltração e ultrafiltração. Neste trabalho membranas de poliamida 66 (PA 66) foram preparadas pelo método de inversão de fases e caracterizadas para aplicação em processos de ultrafiltração. As membranas de PA 66 foram preparadas utilizando dois solventes diferentes, ácido fórmico (AF) e ácido clorídrico (HCl) e água como não-solvente. A análise por Espectroscopia de Infravermelho com Transformada de Fourier (FT-IR) mostrou que a estrutura química da PA 66 não foi alterada com o uso dos solventes na preparação das membranas. O ensaio de compactação com água pura realizado a 1500 kPa de pressão revelou que as membranas preparadas em AF sofreram maior compactação na sua estrutura apresentando fluxo de permeado em torno de 17 L.m-2.h-1 enquanto a membrana preparada em HCl apresentou fluxo de 22,2 L.m-2.h-1. Nos ensaios de ultrafiltração (UF), ambas as membranas apresentaram valores de retenção próximos a 70% para albumina de ovo (45 kDa) e 80% para albumina sérica bovina (69 kDa). Com esse resultado, pode-se concluir que ambas as membranas apresentaram ponto de corte nominal para aplicações em processos de UF.

In the present study, polyamide 66 (PA 66) membranes were prepared by phase inversion method and characterized in order to verify their potential application in ultrafiltration processes. PA 66 membranes were prepared using two different solvents, formic acid (FA) and hydrochloric acid (HCl), and water as a non-solvent. Fourier-transform infrared spectroscopy (FT-IR) showed that the chemical structure of PA 66 was not altered by the use of solvents in the preparation of membranes. The compaction experiment with pure water performed at a pressure of 1500 kPa revealed that membranes prepared with FA undergo greater compaction of its structure and had a permeate flux value of approximately 17 L.m-2.h-1 whereas the membrane prepared with HCl had a permeate flux of 22.2 L.m-2.h-1. In the ultrafiltration experiment, both membranes had retention values around 70% for egg albumin and 80% for bovine serum albumin. Based on this result, one concludes that both membranes had nominal cut off values for application in ultrafiltration processes.